Product Details
Place of Origin: China
Brand Name: JIA SHAN
Certification: ISO
Model Number: DIN, ASEM, ISO
Payment & Shipping Terms
Minimum Order Quantity: 100
Price: USD0.2/pcs-USD1/pcs
Delivery Time: 1-5 weekds
Payment Terms: T/T, Western Union
Supply Ability: Batch order abailable
Usage: |
Fastening |
Style: |
Wire Thread Insert |
Size: |
Various Sizes Available |
Head Style: |
Wire Thread Insert |
Strength: |
High |
Finish: |
Plain |
Manufacturer: |
JIA SHAN Hardward Company |
Length: |
As Customisation |
Package: |
Small Packing+Carton Packing+Pallet |
Standard: |
DIN |
Package Quantity: |
100 Pieces |
Shape: |
Wire Thread Insert |
Measurement System: |
INCH, Metric |
Port: |
Shenzhen |
Quality: |
Inspection Before Shipment |
Color: |
As Customisation |
Material: |
Carbon Steel |
Usage: |
Fastening |
Style: |
Wire Thread Insert |
Size: |
Various Sizes Available |
Head Style: |
Wire Thread Insert |
Strength: |
High |
Finish: |
Plain |
Manufacturer: |
JIA SHAN Hardward Company |
Length: |
As Customisation |
Package: |
Small Packing+Carton Packing+Pallet |
Standard: |
DIN |
Package Quantity: |
100 Pieces |
Shape: |
Wire Thread Insert |
Measurement System: |
INCH, Metric |
Port: |
Shenzhen |
Quality: |
Inspection Before Shipment |
Color: |
As Customisation |
Material: |
Carbon Steel |
M12 M16 Red Blu Green Carbon steel Wire Thread Insert Customized Anodizing finishing
Product Description:
Applications:
Steel types:
| No. | C% | Cr% | Ni % | Mo % |
| 304 | 0.07 | 17.5-19.5 | 8.0-10.5 | / |
| 316 | 0.08 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 |
| 301 | 0.15 | 16.0-18.1 | 6-8 | / |
| 310 | 0.08 | 24-26 | 19-22 | / |
| 304L | 0.03 | 18-20 | 8-12 | / |
| 316L | 0.03 | 16-18 | 10-14 | 2-3 |
| 321 | 0.08 | 17-19 | 9-12 | / |
201, 304, 316 are austenitic stainless steel, according to the performance of the non-magnetic, some of the performance of the weak magnetic because of the smelting of the composition of the segregation or improper heat treatment leads to the austenite in a small amount of martensite or ferrite. Austenitic stainless steel corrosion resistance comes from the formation of chromium oxide protective layer on the metal surface. When the material temperature is heated to 450 degrees -900 degrees, the structure changes, will form chromium carbide along the edge of the crystal and can not form a protective layer of chromium oxide, thus reducing the corrosion resistance, this is also known as ‘intergranular corrosion’. As a result, there are 304L and 316L, the two due to the low carbon content also reduces the intergranular corrosion. In particular, the higher susceptibility to intergranular corrosion does not mean that non-low carbon content is more susceptible to corrosion, in a highly chlorinated environment, this susceptibility is also higher.